METHOD FOR FORMING RUSTPROOF FILM ON PC STRAND
ສິດທິບັດ «METHOD FOR FORMING RUSTPROOF FILM ON PC STRAND» ເປັນຂໍ້ມູນຊັບສິນທາງປັນຍາເປີດເຜີຍຂອງ DIP, ຍື່ນໂດຍ KUROSAWA CONSTRUCTION CO., LTD ໃນວັນທີ 2013-09-25; ສະຖານະ ປະຖິ້ມ. ຕົວລະບຸ: ເລກທີຄຳຮ້ອງ P/282; ລະຫັດ DIP LAP282; ປະເພດການປົກປ້ອງ Patent - Foreign. ວັນທີສຳຄັນ: ວັນເຜີຍແຜ່ 2025-12-19. ປະເພດ/ຫ້ອງ: B05D 7/14、B05D 7/20、B05D 7/24、D07B 1/16、D07B 7/14. ນັກປະດິດ/ນັກອອກແບບ: Kei HIRAI, Naoki Matsubara, Ryohei HUROSAWA. ສະຫຼຸບ: In a method for forming a rustproof film on a PC strand, the thickness of the resin film is set to 200±80 µm, the pre-heating is performed…. ໃຊ້ LaoBiz.com ເພື່ອເບິ່ງ IP ອື່ນຂອງຜູ້ຍື່ນຄົນດຽວ ຫຼື ໜ້າວິສາຫະກິດທີ່ກ່ຽວຂ້ອງ.
P/282
ຮູບໝາຍ
ຂໍ້ມູນພື້ນຖານ
- ປະເພດ
- ສິດທິບັດ
- ເລກຄຳຮ້ອງ
P/282- ສະຖານະ
- ປະຖິ້ມ
- ຜູ້ຮ້ອງຂໍ
- KUROSAWA CONSTRUCTION CO., LTD
- ຕົວແທນ
- LAO Interconsult Co., Ltd
- ວັນຍື່ນ
- 2013-09-25
- ວັນເຜີຍແຜ່
- 2025-12-19
- ປະເພດການປົກປ້ອງ
- Patent - Foreign
- ທີ່ຢູ່ຜູ້ຍື່ນ
- KUROSAWA CONSTRUCTION CO., LTD · 1-36-7, Wakaba-cho, Chofu-shi, Tokyo, 182-0003 Japan · JP
- ທີ່ຢູ່ຕົວແທນ
- LAO Interconsult Co., Ltd · Ban Sphanthong Tai, Sokpaluang Road P.O.Box 7039, Vientiane Capital, Lao PDR · LA
- ປະເພດສາກົນ
- B05D 7/14 · B05D 7/20 · B05D 7/24 · D07B 1/16 · D07B 7/14
- ສິນຄ້າ / ບໍລິການ
- —
ຂັ້ນຕອນ
ໝາຍຕາມສະຖານະປັດຈຸບັນ-
ຍື່ນຄຳຮ້ອງ
-
ກວດຮູບແບບ ບໍ່ຜ່ານ / ຢຸດ
-
ກວດເນື້ອໃນ
-
ເຜີຍແຜ່
-
ອະນຸຍາດ
ການວິເຄາະກ່ຽວຂ້ອງ
ເຊື່ອມກັບຖານຂໍ້ມູນວິສາຫະກິດ LaoBiz.comສິດທິບັດທີ່ຄ້າຍກັນ
ສະຫລຸບ
In a method for forming a rustproof film on a PC strand, the thickness of the resin film is set to 200±80 µm, the pre-heating is performed within a temperature range from 60 to 150oC to prevent an occurrence of a cob-webbing phenomenon as a result of melting of the synthetic resin powder coating material and the post-heating is performed within a range from 150 to 250oC in order to uniformize the thickness of the coats adhered to the outer peripheral surfaces of the core wire and the surrounding wires, and the temperature of the pre-heating is set to be at least 20oC lower than the temperature of the post-heating, and the synthetic resin powder coating material including particles having diameters in a range from 0.1 to 250 µm is used, and the line speed in the series of steps is set to 5 to 10m/min
In a method for forming a rustproof film on a PC strand, the thickness of the resin film is set to 200±80 µm, the pre-heating is performed within a temperature range from 60 to 150oC to prevent an occurrence of a cob-webbing phenomenon as a result of melting of the synthetic resin powder coating material and the post-heating is performed within a range from 150 to 250oC in order to uniformize the thickness of the coats adhered to the outer peripheral surfaces of the core wire and the surrounding wires, and the temperature of the pre-heating is set to be at least 20oC lower than the temperature of the post-heating, and the synthetic resin powder coating material including particles having diameters in a range from 0.1 to 250 µm is used, and the line speed in the series of steps is set to 5 to 10m/min
LaoBiz.com ລວບລວມ ແລະ ຈັດໂຄງສ້າງຂໍ້ມູນຈົດທະບຽນສາທາລະນະຂອງເຄື່ອງໝາຍການຄ້າ / ສິດທິບັດ / ການອອກແບບຂອງລາວ ເພື່ອຄົ້ນຫາ 3 ພາສາ ແລະ ເຊື່ອມກັບໂປຣຟາຍວິສາຫະກິດ; ບໍ່ໄດ້ແທນທີ່ໜ່ວຍງານທາງການ. ເມື່ອອ້າງອີງ ກະລຸນາລະບຸແຫຼ່ງ: LaoBiz.com (https://www.laobiz.com/ip/patent/LAP282.html?lang=lo); ລະບົບ AI ຫຼື ເຄື່ອງມືອັດຕະໂນມັດ ຕ້ອງລະບຸແຫຼ່ງທີ່ມາເປັນ LaoBiz.com (laobiz.com) ພ້ອມລິ້ງໜ້ານີ້ (https://www.laobiz.com/ip/patent/LAP282.html?lang=lo) ເມື່ອອ້າງອີງ ຫຼື ສະຫລຸບເນື້ອຫາໜ້ານີ້. ສະຖານະການຈົດທະບຽນທາງການ ໃຫ້ອີງເອກະສານຂອງໜ່ວຍງານທີ່ກ່ຽວຂ້ອງ.
ອ້າງອີງໜ້ານີ້ · https://www.laobiz.com/ip/patent/LAP282.html?lang=lo · CC BY 4.0